Due to different uses, the quality requirements of refractory clay vary from industry to industry. As the refractory clay used for the refractory material, the quality requirements are shown in Table 1. For hard clay clinker as refractory materials used, the unit according to the ministerial standard metallurgical industry (YB2211-82), technical requirements of Table 2. The content of impurities in the product shall not exceed 3% for special grades and 4% for other grades; limestone , loess and other high-calcium, high- iron and other foreign inclusions shall not be mixed into the product. There is no uniform standard for the technical requirements of high alumina clay in the grinding industry. The requirements of Zhengzhou Abrasives Factory (1977) are: Al 2 O 3 ≥67%, SiO 2 ≤10%, CaO+MgO<1, Al 2 O 3 / SiO 2 values greater than 9; magnesium aluminum Shenyang Institute (1983) requirements are: Al 2 O 3 ≥70%, Fe 2 O 3 ≤5%, TiO 2 ≤4.5%, CaO + MgO≤1.0%, The Al 2 O 3 /SiO 2 value is greater than 12. Ductile Iron Sand Castings,Sand Casting,Malleable Cast Iron Sand Casting Product,Cast Iron Sand Casting Hebei Chunfeng International Trade Co., Ltd , https://www.chunfengenergy.com
For a high-aluminum refractory bauxite is used, the technical standard (YB2212-82) As shown in Table 3. In addition to the physical and chemical indicators listed in the table, it is also required that: products that are contacted with coal and calcined, do not exceed 10% of the sieved material through the 10mm standard sieve, and the products calcined by the rotary kiln and the external combustion kiln pass through the 5mm standard sieve. The amount of impurities in the sieve is not more than 10%; the content of impurities in the product is not more than 4%; the adjacent grades are allowed to be no more than 10% in the same grade; limestone, loess and other high-calcium, high-iron and other foreign objects may not be mixed into the product.
The technical requirements of the cement industry for high-aluminum clay are as follows: Al 2 O 3 ≥72%, SiO 2 ≤6%, Fe 2 O 3 ≤2% according to the Shenyang Aluminum-Magnesium Design Institute (1983).